Gradus effectus coagmentatis carbide - KEDEL GRADUS YN

Gradus Partium Carbidi Cementati, Proprietates (KD/QI/ZJ001-2020)
Gradus	Compositio (% ponderis)			Proprietates Physicae							Aequivalens domestico
	Compositio (% ponderis)			Densitas g/cm³ (±0.1)	Duritia HRA (±0.5)	TRS Mpa (min)	Porositas			Magnitudo granorum (μm)
	WC	Ni	Alia	Densitas g/cm³ (±0.1)	Duritia HRA (±0.5)	TRS Mpa (min)	A	B	C	Magnitudo granorum (μm)
KDN6	93.8	6.0	0.2	14.6-15.0	89.5-90.5	MDCCC	A02	B00	C00	0.8-2.0	YN6
KDN7	92.8	7.0	0.2	14.4-14.8	89.0-90.0	1900	A02	B00	C00	0.8-1.6	YN7
KDN8	91.8	8.0	0.2	14.5-14.8	89.0-90.0	MMCC	A02	B00	C00	0.8-2.0	YN8
KDN12	87.8	12.0	0.2	14.0-14.4	87.5-88.5	2600	A02	B00	C00	0.8-2.0	YN12
KDN15	84.8	15.0	0.2	13.7-14.2	86.5-88.0	2800	A02	B00	C00	0.6-1.5

Gradus effectus coagmentatis carbide - KEDEL GRADUS YG

Gradus Partium Carbidus Cementati, Proprietates (KD/QI/ZJ001-2020)
Gradus	Compositio (% ponderis)				Proprietates Physicae							Aequivalens domestico
	Compositio (% ponderis)				Densitas g/cm³ (±0.1)	Duritia HRA (±0.5)	TRS Mpa (min)	Porositas			magnitudo granorum (μm)
	WC	Co	Ti	TaC	Densitas g/cm³ (±0.1)	Duritia HRA (±0.5)	TRS Mpa (min)	A	B	C	magnitudo granorum (μm)
KD115	93.5	6.0	-	0.5	14.90	93.0	2700	A02	B00	C00	0.6-0.8	YG6X
KD335	89.0	10.5	-	0.5	14.40	91.8	3800	A02	B00	C00	0.6-0.8	YG10X
KG6	94.0	6.0	-	-	14.90	90.5	2500	A02	B00	C00	1.2-1.6	YG6
KG8	92.0	8.0	-	-	14.75	90.0	3200	A02	B00	C00	1.2-1.6	YG8
KG9	91.0	9.0	-	-	14.60	89.0	3200	A02	B00	C00	1.2-1.6	YG9
KG9C	91.0	9.0	-	-	14.60	88.0	3200	A02	B00	C00	1.6-2.4	YG9C
KG10	90.0	10.0	-	-	14.50	88.5	3200	A02	B00	C00	1.2-1.6	YG10
KG11	89.0	11.0	-	-	14.35	89.0	3200	A02	B00	C00	1.2-1.6	YG11
KG11C	89.0	11.0	-	-	14.40	87.5	tria milia	A02	B00	C00	1.6-2.4	YG11C
KG13	87.0	13.0	-	-	14.20	88.7	3500	A02	B00	C00	1.2-1.6	YG13
KG13C	87.0	13.0	-	-	14.20	87.0	3500	A02	B00	C00	1.6-2.4	YG13C
KG15	85.0	15.0	-	-	14.10	87.5	3500	A02	B00	C00	1.2-1.6	YG15
KG15C	85.0	15.0	-	-	hora quarta decima	86.5	3500	A02	B00	C00	1.6-2.4	YG15C
KD118	91.5	8.5	-	-	14.50	93.6	3800	A02	B00	C00	0.4-0.6	YG8X
KD338	88.0	12.0	-	-	14.10	92.8	4200	A02	B00	C00	0.4-0.6	YG12X
KD25	77.4	8.5	6.5	6.0	12.60	91.8	MMCC	A02	B00	C00	1.0-1.6	P25
KD35	69.2	10.5	5.2	13.8	12.70	91.1	2500	A02	B00	C00	1.0-1.6	P35
KD10	83.4	7.0	4.5	4.0	13.25	93.0	MM	A02	B00	C00	0.8-1.2	M10
KD20	79.0	8.0	7.4	3.8	12.33	92.1	MMCC	A02	B00	C00	0.8-1.2	M20

Servitium Customizationis

Officia ad singulorum necessitates aptata accipere possumus. Fabricare possumus OEM secundum delineationes tuas et ODM secundum necessitates tuas.

Celerrimus tempus traditionis productorum ad singulorum necessitates aptatorum est septem dies.

Processus Productionis

1. Pulvis carburi tungsteni cum diverso gradu et magnitudine granorum

2. Molitura globulorum (processus paraffini et processus alcoholis)

3. Turris pulveris siccatio

4. Prelum formans

5. Sinterizatio fornacis sinterationis pressionis humilis

6. Curatio superficiei - Sabulatio

7. Inspectio

8. Trituram perficias

9. Purgatio et sarcinatio

10. Inspectio officinae

Condicio Reditus

Pro problematis qualitatis productorum a societate nostra confirmatis, nova producta quae inspectionem superaverunt tempestive denuo edemus, et sumptus translationis a societate nostra ferentur. Producta non qualificata tempestive reddemus.

Servitium Logisticum

Cum quattuor societatibus internationalibus praecipuis, DHL, FedEx, UPS et TNT, cooperamur. Generaliter, tempus translationis inter dies septem et decem est.

Vecturam etiam via, ferrivia, aerea et maritima accipimus.

Cura Qualitatis

Tempus pignoris qualitatis productorum nostrorum plerumque unum annum est. Si intra tempus pignoris problemata qualitatis exstiterint, ea reddere et substituere possumus, sed problema damni producti ex usu improprio orti non sustinebimus.

Qualitatis Moderatio

Materiae rudis acquirenda --- Productio vacui --- Machinatio finiendi productum --- Processus inductionis

1. Id est, WC, Co, Ta, Nb, Ti, aliaeque materiae carburi cementati ad productionem in officinam emptae sunt ad qualitatem inspiciendam.

2. Congeries massarum, molendinum globulorum, granulatio, pressio, sinterizatio, probatio proprietatum physicarum inanium, et in processum proximum post probationem superatam ingrediuntur.

3. Pars bruta per processus processus, ut circulum externum, foramen internum, superficiem extremam, filum, trituram formationis et tractationem marginis, transit, et post inspectionem, processum proximum ingreditur.

4. Inter societates cooperationis strategicae in materia obductionis sunt Balchas, Aenbond, Suzhou Dingli, et cetera. Obductio, postquam inspectionem superaverit, in apotheca conservabitur.

Servitium