Virgae carbidae congestae adhiberi possunt ad molendina finem faciendam, varia terebra frena, automobile dromonem specialem, machinam specialem caedentem, horologiam, serratores speciales processus, integram verticalem molarem molarem, graviorem et etc. Item, tungstes carbide in mixturam duram fieri possunt. pugnis, mandrellis, centra, ferramenta perforationis.
1. Bonus taedium resistentia, durities superior, subtilitas, melior deformatio et resistentia fractura
2. Provectus automatic extrusionem apparatu ad producendum
3. HIP sintering et exquisite stridor ad invigilandum, ut bene sit effectus
4. Tam blank et condiciones praesto perfecta
5. Potest pervenire speculi effectum superficies post accurate stridor ac poliuntur
Virgae solidae Carbide (plenitudo) | |||||
Nominal Dia | D(mm) | D(mm) | Longitudo | Dicta | |
D (mm) | Un-humus | h6 | mm | ||
0.5 | 0.7 | 0.5 | 310-330 | ||
0.8 | 1 | 0.8 | 310-330 | ||
1 | 1.2 | 1 | 310-330 | ||
1.5 | 1.7 | 1.5 | 310-330 | ||
1/16" | 1.5875 | 1.8 | 1.5875 | 12" -13" | pollicis magnitudine |
2 | 2.2 | 2 | 310-330 | ||
2.35 | 2.55 | 2.35 | 310-330 | ||
3/32" | 2.38 | 2.6 | 2.38 | 12" -13" | pollicis magnitudine |
2.5 | 2.7 | 2.5 | 310-330 | ||
3 | 3.2 | 3 | 310-330 | ||
1/8" | 3.175 | 3.4 | 3.175 | 12" -13" | inchi magnitudine |
3.5 | 3.7 | 3.5 | 310-330 | ||
5/32 | 3.968 | 4.2 | 3.968 | 12" -13" | inchi magnitudine |
4 | 4.2 | 4 | 310-330 | ||
4.5 | 4.5 | 310-330 | |||
3/16" | 4.7625 | 5 | 4.762 | 12" -13" | pollicis magnitudine |
5 | 5.2 | 5 | 310-330 | ||
5.5 | 5.7 | 5.5 | 310-330 | ||
6 | 6.2 | 6 | 310-330 | ||
1/4" | 6.35 | 6.6 | 6.35 | 12" -13" | pollicis magnitudine |
6.5 | 6.7 | 6.5 | 310-330 | ||
7 | 7.2 | 7 | 310-330 | ||
7.5 | 7.7 | 7.5 | 310-330 | ||
5/16" | 7.937 | 8.2 | 7.937 | 12" -13" | pollicis magnitudine |
8 | 8.2 | 8 | 310-330 | ||
8.5 | 8.7 | 8.5 | 310-330 | ||
9 | 9.2 | 9 | 310-330 | ||
9.5 | 9.7 | 9.5 | 310-330 | ||
3/8" | 9.525 | 9.7 | 9.525 | 12" -13" | pollicis magnitudine |
10 | 10.2 | 10 | 310-330 | ||
10.5 | 10.7 | 10.5 | 310-330 | ||
11 | 11.2 | 11 | 310-330 | ||
7/16" | 11.11 | 11.3 | 11.11 | 12" -13" | pollicis magnitudine |
11.5 | 11.7 | 11.5 | 310-330 | ||
12 | 12.2 | 12 | 310-330 | ||
12.5 | 12.7 | 12.5 | 310-330 | ||
1/2" | 12.7 | 12.9 | 12.7 | 12" -13" | pollicis magnitudine |
13 | 13.2 | 13 | 310-330 | ||
13.5 | 13.7 | 13.5 | 310-330 | ||
14 | 14.2 | 14 | 310-330 | ||
9/16" | 14.288 | 14.5 | 14.288 | 12" -13" | pollicis magnitudine |
14.5 | 14.7 | 14.5 | 310-330 | ||
15 | 15.2 | 15 | 310-330 | ||
15.5 | 15.7 | 15.5 | 310-330 | ||
5/8" | 15.875 | 16.1 | 15.875 | 12" -13" | pollicis magnitudine |
16 | 16.2 | 16 | 310-330 | ||
16.5 | 16.7 | 16.5 | 310-330 | ||
17 | 17.2 | 17 | 310-330 | ||
17.5 | 17.7 | 17.5 | 310-330 | ||
18 | 18.2 | 18 | 310-330 | ||
18.5 | 18.7 | 18.5 | 310-330 | ||
19 | 19.2 | 19 | 310-330 | ||
3/4" | 19.05 | 19.3 | 19.05 | 12" -13" | pollicis magnitudine |
19.5 | 19.7 | 19.5 | 310-330 | ||
20 | 20.2 | 20 | 310-330 | ||
20.5 | 20.7 | 20.5 | 310-330 | ||
21 | 21.2 | 21 | 310-330 | ||
21.5 | 21.7 | 21.5 | 310-330 | ||
22 | 22.2 | 22 | 310-330 | ||
22.5 | 22.7 | 22.5 | 310-330 | ||
23 | 23.2 | 23 | 310-330 | ||
23.5 | 23.7 | 23.5 | 310-330 | ||
24 | 24.2 | 24 | 310-330 | ||
24.5 | 24.7 | 24.5 | 310-330 | ||
25 | 25.2 | 25 | 310-330 | ||
1" | 25.4 | 25.7 | 25.4 | 12" -13" | pollicis magnitudine |
26 | 26.3 | 26 | 310-330 | ||
27 | 27.2 | 27 | 310-330 | ||
28 | 28.2 | 28 | 310-331 | ||
29 | 29.2 | 29 | 310-333 | ||
30 | 30.2 | 30 | 310-334 | ||
31 | 31.2 | 31 | 310-335 | ||
1-1/4" | 31.75 | 32 | 31.75 | 12" -13" | pollicis magnitudine |
32 | 32.2 | 32 | 310-336 | ||
33 | 33.2 | 33 | 310-337 | ||
34 | 34.2 | 34 | 310-338 | ||
35 | 35.2 | 35 | 310-339 | ||
36 | 36.2 | 36 | 310-340 | ||
37 | 37.2 | 37 | 310-341 | ||
38 | 38.2 | 38 | 310-342 | ||
1-1/2" | 38.1 | 38.4 | 38.1 | 12" -13" | pollicis magnitudine |
39 | 39.2 | 39 | 310-343 | ||
40 | 40.2 | 40 | 310-344 | ||
42 | 42.2 | 42 | 310-344 |
Gradus Introductio ad Carbide Rods | |||||||
Gradus | Co% | WC frumenti magnitudine | HRA | HV | Densitas (g/cm* | Tendens robur MPa) | Fractura durities(MNm-3/2) |
KT10F | 6 | Submicron | 92.9 | 1840 | 14.8 | 3800 | 10 |
KT10UF | 6 | superfine | 93.8 | 2040 | 14.7 | 3200 | 9 |
KT10NF | 6 | nanometer | 94.5 | 2180 | 14.6 | 4000 | 9 |
KT10C | 7 | Fine | 90.7 | 1480 | 14.7 | 3800 | 12 |
KT11F | 8 | Submicron | 92.3 | 1720 | 14.6 | 4100 | 10 |
KT11UF | 8 | superfine | 93.5 | 1960 | 14.5 | 3000 | 9 |
KT12F | 9 | superfine | 93.5 | 1960 | 14.4 | 4500 | 10 |
KT12NF | 9 | nanometer | 94.2 | 2100 | 14.3 | 4800 | 9 |
KT15D | 9 | Submicron | 91.2 | 1520 | 14.4 | 4000 | 13 |
KT15F | 10 | Submicron | 92.0 | 1670 | 14.3 | 4000 | 11 |
KT20F | 10 | Submicron | 91.7 | 1620 | 14.4 | 4300 | 11 |
KT20D | 10 | Submicron | 92.0 | 1670 | 14.3 | 4500 | 11 |
KT25F | 12 | superfine | 92.4 | 1740 | 14.1 | 5100 | 10 |
KT25EF | 12 | superfine | 92.2 | 1700 | 14.1 | 4800 | 10 |
KT25D | 12 | superfine | 91.5 | 1570 | 14.2 | 4200 | 13 |
KT37NF | 15 | nanometer | 92.0 | 1670 | 13.8 | 4800 | 10 |